Comparative Morphologic Evaluation and Occluding Effectiveness of Nd: YAG, CO2 and Diode Lasers on Exposed Human Dentinal Tubules: An Invitro SEM Study ZC66-ZC70
Dr. Mini Saluja,
Faculty of Dental Sciences, SGT University, Department of Periodontology, Chandu- Budhera, Gurgaon- Badli Road,
Gurgaon, Haryana-122505, India.
Introduction: Dentinal hypersensitivity is one of the most common problem, encountered in dental practice but has least predictable treatment outcome. The advent of lasers in dentistry has provided an additional therapeutic option for treating dentinal hypersensitivity. Although various lasers have been tried over a period of time to treat dentinal hypersensitivity, but still the doubt persist as to which laser leads to maximum dentinal tubular occlusion and is most suitable with minimal hazardous effects.
Aim: To compare the effects of Nd: YAG, CO2 and 810-nm diode lasers on width of exposed dentinal tubule orifices and to evaluate the morphologic changes on dentinal surface of human tooth after laser irradiation by scanning electron microscope (SEM).
Materials and Methods: Forty root specimens were obtained from ten freshly extracted human premolars, which were randomly divided into four groups of ten each. Group I: control group treated with only saline, Group II: Nd:YAG laser, Group III: CO2 laser and Group IV: 810-nm diode laser. The specimens were examined using SEM. After calculating mean tubular diameter for each group, the values were compared statistically using parametric one-way ANOVA test and Turkeyâ€™s post hoc multiple comparison test.
Results: All the three lased groups showed a highly statistical significant result with p-value of <0.001 as compared to non-lased group. On intergroup comparison within the lased groups, all the three groups showed statistically significant difference in the reduction of dentinal tubular diameter (p-value < 0.001).
Conclusion: Nd: YAG laser was found to be most effective, followed by the CO2 laser and 810-nm diode laser was found to be least effective. The morphologic changes like craters, cracks and charring effect of the dentine were seen maximum by the use of CO2 laser.