Effect of Ageing, Staining and Polishing on the Colour Stability of a Single, a Group Shade and Nano Fill Dental Composite: An In-vitro Study
Correspondence Address :
Fatin A Hasanain,
PO Box 80209, Jeddah, Western Region, Saudi Arabia.
E-mail: fhasanain@kau.edu.sa
Introduction: With the increase in aesthetic requirements, more people are requesting tooth coloured fillings. An anterior restoration is deemed unacceptable if its colour changes significantly.
Aim: To assess the colour stability of a single shade, a group shade and a nano fill dental resin composite which comes in multiple shades.
Materials and Methods: This in-vitro study was conducted in the month of August 2021 at the Advanced Technology Dental Research Laboratory at the King Abdul Aziz University, Jeddah, Western region, Saudi Arabia. Three composites were tested; a single shade (Omnichroma), a group shade (Optishade Light (OL) and Optishade Medium (OM)) and a conventional nano fill (Z350) 40 cylindrical discs (10 mm in diameter and 2 mm in depth) were fabricated in total. Each material and shade to be tested had 10 samples per group (n=10). The materials were aged in a thermocycler for 5000 cycles then stained with either green tea or coffee for six days. Upon completion of the staining protocol, they were then polished with soflex diamond polishing system. Colour measurements were taken at each stage, calculated and compared. Mixed model repeated Analysis Of Variance (ANOVA) was performed to determine significance of the colour change (?E00) between materials and treatments and Bonferroni test was used for multiple comparison between groups.
Results: The effect of ageing varied according to individual material; Z350 had lower ?E00 when compared to other materials. After staining with tea, it was found that Z350 and Omnichroma exhibited a significant change (p<0.05) in ?E00 when compared to OL. Polishing improved the ?E00 in all the materials. All green tea-stained materials with the exception of Omnichroma returned to a clinically acceptable E00 after polishing. After polishing coffee stained samples, OL and OM remained above the clinically acceptable threshold while Z350 and omnichroma were returned to a clinically acceptable level.
Conclusion: All the materials showed a change in ?E00 after ageing, with OM and Z350 being the only materials to exhibit a clinically acceptable change. While polishing decreased ?E00 in all the materials, it did not return them all to a clinically acceptable level. Thus, polishing helps improve the appearance of stained restorations but may not be enough to completely remove stains, even in newly introduced direct aesthetic dental materials.
Aesthetic dental filling, Discolouration, Omnichroma, Optishade
Currently the material of choice for direct restorations among most dental practitioners is dental resin composites (1),(2). This is due to their excellent aesthetics and material properties (3). Providing the patient with a functional, yet imperceptible aesthetic restoration is the ultimate goal of a dental practitioner. As a means to that end, dental resin composite systems were created with a myriad of shades to enable the clinician to match the surrounding tooth structure seamlessly. Unfortunately, the placement of perfectly camouflagued restorations remains an unattained goal in many clinical cases (4). Recently, in an attempt to make the process of shade selection easier while improving the final result, manufacturers created dental resin composite materials which have one or very few shades to replace the multiple shades used previously (5). These materials are called ‘single shade’ or ‘group shade’ dental resin composites and have been found to blend into the surrounding tooth structure very well (6),(7).
Among the requirements for a successful aesthetic restoration is that it maintain its colour and shade [8,9]. Colour change is among the main reasons for the replacement of anterior dental resin composite restorations (9). Some of the most common reasons for such discolouration include the consumption of dietary substances such as tea and coffee [10-13]. These drinks stain teeth as well as dental resin composite restorations and can change the perceived shade of the filling (10),(14). Although the most recent formulations of dental resin composites often maintain colour over extended periods of time, they are still prone to staining and discolouration. Chairside polishing is a method frequently used to decrease the appearance of stains in mildly discoloured teeth and restorations (15),(17),(18). While other studies have recorded the effect of polishing pastes or chairside polishing on stains in dental resin composites, they did so in the absence of ageing and for varying periods of time (16),(17),(18). This study aimed to mimic the clinical scenario by ageing the materials as well as simulate a typical biannual dental visit prior to testing if polishing would improve the discolouration in a single and group shade dental resin composite. The colour stability was tested after ageing, staining with green tea or coffee and subsequently polishing. The null hypothesis was that none of the treatments would affect the colour stability of the materials, irrespective of the material used.
This in-vitro study was conducted in the month of August 2021 at the Advanced Technology Dental Research Laboratory at the King Abdul Aziz University, Jeddah, Western region, Saudi Arabia with Ethical approval number 071-03-19. Three commercially available, widely used dental resin composite systems were chosen. The details of each system as given by their respective manufacturers are shown in (Table/Fig 1). Two of the systems used in this study, Omnichroma and Optishade, possess colour adjustment potential according to their manufacturers. The Omnichroma is supplied in one shade only, while Optishade has three available shades, of which OL and OM were chosen to simulate the filling of anterior teeth. The third composite system tested, Z350, is among the most commonly used in dental practices. Z350 does not have a chameleon effect. A2 is one of the most popular shades so it was chosen to be included in the study.
Study Procedure
In total 40 cylindrical discs (10 mm in diameter and 2 mm in depth) were fabricated. Each material and shade to be tested had 10 samples per group (n=10). The specimens were made using a custom-made silicon mould. The mould was placed on a glass microscope slide which rested on a glass slab. The composite was then adapted into the mould and covered with another glass slide to remove the excess. The specimen was immediately light cured for 20 seconds on the top and bottom using a LED Light Curing Unit (LCU) (3M ESPE Elipar, St Paul, MN, USA). The power density was measured with digital radiometer (Bluephase Meter II, Ivoclar, Amherst, NY, USA) at 1100 mW/cm2 immediately before specimen preparation.The specimen preparation setup is illustrated while showing a completed specimen (Table/Fig 2),(Table/Fig 3). The methodology for the study is illustrated in (Table/Fig 4).
Specimens were then polished using the sof-lex diamond polishing system. The colour parameters of each sample were then determined using a clinical spectrophotometer (Vita Easyshade Advance 5, Vita Zahnfabrik, Germany). As per the manufacturer’s instructions, the spectrophotometer was calibrated prior to use using the white calibration plate provided. To determine a specimen’s colour parameters, the measurement tip was placed in direct contact and perpendicular to the sample surface. A positioning jig was used to place the measuring tip on each specimen in a reproducible manner. Each sample was measured three times and the mean values were used for analysis. Recalibration was done after 10 samples were analysed.
Ageing procedure: All the samples were artificially aged in a custom made thermocycling unit. The thermocycling chambers had a temperature of 5°C and 55°C (15 seconds dwell time in each temperature chamber) for 5000 cycles (19).
Staining and polishing samples: Each material group was divided into two (n=5) and immersed in one of two staining solutions; coffee (1 teaspoon coffee in 180 mL of just boiled water, Nescafe Classic, USA) or green tea (one teabag brewed in just boiled water for two minutes, (Twinings Green Tea, Twinings, UK). It has been reported that the average coffee drinker consumes 3.2 cups per day and spends 15 minutes drinking a single cup (13). Thus, storage in coffee for 24 hours simulates about one month of coffee consumption (13). The specimens were stored in their respective staining solutions in an incubator (Memmert, Schwabach, Germany) at 37°C for six days, which represents approximately six months of tea or coffee drinking. After the immersion time was completed, the samples were removed from their respective containers, rinsed for 10 seconds, air dried and then their colour parameters were recorded. Samples were then polished using sof-lex diamond polishing system (3 M ESPE) and their colour parameters measured once again. The samples were placed in separate containers to ensure that the same sample was measured each time.
Measurement of colour change: Baseline shades for all samples were taken immediately after sample preparation was completed. The colour parameters of each sample was measured at four different time points; immediately after preparation (T0), after ageing (T1), after staining (T2) and finally after polishing (T3). Samples were measured in the same location in the laboratory each time and a positioning jig was used to standardise the placement of the probe on the specimen during measurement of the colour parameters.
Each specimen’s colour change was calculated according to the CIEDE2000 formula (?E00) (20).
The CIEDE2000 colour-difference formula in Microsoft Excel was used for this analysis as proposed by Sharma G et al., (21).
To determine the Threshold of Perceptability (PT) and Threshold of Acceptability (AT), the parameters described by Paravina RD et al., were used (22). The CIEDE2000 (?E00) values in dentistry were 50:50 PT was found to be 0.8 and 50:50% AT was found to be 1.8 (22). Thus, the colour change was considered undetectable when ?E00 ≤0.8 and considered clinically unacceptable when ?E00 ≥1.8 (22).
Statistical Analysis
Mixed model repeated ANOVA was performed to determine ?E00 between materials and treatments and Bonferroni test was used for multiple comparison between groups. Statistical software, Statistical Package for the Social Sciences (SPSS) Ver. 17 (IBM Inc., Armonk, NY, USA) was utilised at 0.05 significance level.
The mean ?E00 and standard deviations of all the materials after ageing, staining and polishing are shown in (Table/Fig 5). The mixed model repeated ANOVA showed that the staining solution, material and polishing all had a statistically significant effect on ?E00 (p<0.001) as shown in (Table/Fig 6). Furthermore, the statistical difference is material dependant in all the processes which the samples were subjected to. Pairwise comparisons are shown in (Table/Fig 7). It shows that there is a significant difference between Z350 and Omni. Z350 showed significantly less of a change in ?E00 values after ageing. Z350 and Omni both had significantly higher ?E00 values (p<0.001) when stained with green tea, while coffee did not have a significant effect on the value of ?E00. On comparison with Z350, OL showed significantly higher ?E00 values when stained with coffee (p<0.05). Polishing coffee stained samples showed no significant differences during pairwise comparisons as shown in (Table/Fig 7).
In spite of the significant differences or lack of it, OL, Omni and Z350 all showed a clinically unacceptable change in ?E00 when stained with either green tea or coffee. When aged, OM had a ?E00 of 1.5, and 1.6 when stained with tea, which was reduced to 1.4 after polishing. Staining OM with coffee increased ?E00 to 3.1 which decreased to 2.1 after polishing. Regardless of the staining solution, differencepolishing in Z350 reduced the ?E00 to below 1.8. With the exception of Omni, all the materials had ?E00 of less than 1.8 after polishing green tea-stained samples. In the coffee-stained samples, polishing Omni and Z350 resulted in a clinically acceptable ?E00. Both OL and OM had ?E00 of above 1.8.
Aesthetic restorations are frequently requested and placed in dental practices (3). Optishade and Omni are both aesthetic restorative materials that have recently been introduced into the dental marketplace. Z350 is a nano composite commonly used in dental practices with a long track record, thus it was chosen for this work. A vital marker of the success of an aesthetic restoration is its colour stability (23). Colour stability has been frequently evaluated by immersion of the test materials in staining solutions (12),(14),(18),(23),(24),(25). The choice of staining solutions was derived from commonly consumed beverages. Coffee is among the most commonly consumed beverages and green tea is becoming more popular among health conscious individuals (23),(26). The Commission Internationale de l’Eclairage (CIELAB) colour difference formula has been used by several studies to evaluate colour stability (11),(14),(23). However, the CIEDE2000’s formula corrects for small colour variations and is a recommended formula which improves the perception of the visual colour difference (7),(27). Thus, CIEDE2000 was used in this work (22).
As soon as a material is placed in a patient’s mouth, it begins to age. In an effort to better simulate the clinical situation in the laboratory, all the materials tested were aged prior to staining. It has been reported that 10,000 cycles in a thermocycling machine are equivalent to one year of clinical function, thus the samples were aged for 5,000 cycles to simulate approximately six months of clinical service (28). The samples were placed in the staining solution for six days which simulated six months of the consumption of the chosen beverage (13). This study simulated the scenario of biannual dental check-ups, as recommended by dentists.
In this study, the null hypothesis was rejected because there was a significant difference in ?E00 in between the materials tested and the procedures that they were subjected to. Z350 and OM had a clinically imperceptible change in ?E00 after ageing, with Z350 being significantly different from OM. OL and Omni had ?E00 of just over 1.8, making their colour change clinically apparent and just over the acceptable threshold. Pairwise comparisons with OL showed that staining with green tea significantly increased ?E00 in Z350 and Omni while there was no significant difference in OM. This is in agreement with researchers who found that tea stained dental resin composites more than coffee did (13). The reason given for the staining potential of tea is the presence of tannins. This is an interesing finding as green tea has been found to have a lower percentage of tannins (3.1%) when compared with black tea (13.36%) (29). Despite the lower tannin content, both Z350 and Omni showed a significant difference after being stained with green tea. The lower tannin content may explain the positive effect polishing had on the green tea stained samples. The results of this study showed that staining with coffee caused a greater increase in ?E00 in OL, when compared to Omni or Z350. This is in agreement with a previous work by AlHamdan EM et al., which found the colour stability of Omni to be comparable to Z350 when staining with coffee (24). The OL and OM findings are in agreement with studies which found that coffee stained more than tea (11),(30). These findings are most likely due to the differences in the chemistry of the staining solutions themselves and their interactions with the individual material. Both Z350 and Omni have a similar filler loading and Urethane Dimethacrylate (UDMA) in their resin composition (31),(32), while OL and OM are two shades of the same material, with identical filler loading and no UDMA in the composition of their resin matrix (33). Even though the difference was not significant, OL appeared more stained when compared to OM. OL is the lighter shade and thus it is expected to stain more than a darker shade as has been reported previously (34).
As mentioned in the results section, all the materials exhibited clinically unacceptable changes in ?E00 after staining regardless of whether a significant difference was found or not. Polishing the samples decreased the ?E00 in all the materials to varying levels. After polishing, Z350 had a ?E00 of less than 1.8 regardless of the staining solution. Polishing coffee stained Omni also exhibited a clinically acceptable ?E00. OL and OM also showed a decrease to below 1.8 after polishing the green tea stained samples. These results are in agreement with researchers who found that extrinsic stains decreased after polishing (18),(25).
The absorption of colourants found in the different foods and beverages is a cause of staining in the oral environment. Water is the carrier for the staining pigments to travel into the resin matrix. Thus, water sorption has a major impact on colour stability and it is affected by the hydrophilicity of the resin matrix as well as the resin matrix to filler ratio. The higher the ratio of resin matrix to fillers within the restorative material, the more the water sorption and subsequent colour change (14),(35). It has been found that UDMA resin composites tend to have better colour stability when compared with Bisphenol-A-Glycidyl-Methacrylate Bis-GMA as UDMA has lower water sorption (14). Resin based materials which contain Bis-GMA or Triethyleneglycol Dimethacrylate (TEGDMA) are hydrophilic and thus may show higher rates of absorption (36),(37),(38).
In this study, the material without Bis-GMA, Omni, did not show more colour stability than all the other materials.
As with most processes in the oral cavity, multiple factors affect the final outcome. The results of this work may be better explained by looking at both the filler loading and resin composition. The material with the lowest filler loading in this study was Z350 at 78.5% by weight. The next highest filler loading was Omni at 79% by weight. OL and OM were both 81% (31),(32),(33). Thus, Z350 showed the most change when stained with tea, while OL and OM showed a smaller change.
The author has suggested that it is possible to remove stains on dental composite resin restorations through polishing (38). In this work, that was true for Z350 regardless of which solution stained it, OL and OM after tea staining, and Omni after coffee staining. Polishing did not fully remove the stains for OL and OM after coffee staining or Omni after green tea stained it. It did, however, markedly decrease ?E00 in all the materials tested. This is in agreement with a previous study which showed that even though the staining decreased, it was not completely removed (15).
Limitation(s)
As with all in-vitro studies, the limitation of this work is that it is not a complete simulation of the clinical situation, as in the mouth several factors are involved, such as toothbrushing and mastication along with ingestion of other types of food and drink. The staining solutions were also placed for an approximation of six months, which is a relatively short amount of time to judge the staining potential of a restoration. Further research involving the addition of toothbrushing to the processes which the samples are subjected to and a longer period of immersion would yield more information regarding the behaviour of the materials.
Within the limitations of this study, several conclusions may be drawn regarding the colour stability of the materials tested. Among the most important for the clinician is that all the materials showed a change ?E00 after ageing, with OM and Z350 being the only materials to exhibit a clinically acceptable change. Then, when the materials were stained for an approximation of six months, nearly all the materials showed clinically unacceptable staining. Only OM showed a clinically imperceptible change when stained with green tea. While polishing decreased ?E00 the regardless of the staining medium, not all the materials went back to a clinically acceptable level of ?E00. Thus, it is important that a clinician is aware that aesthetic dental filling materials are susceptible to a visually apparent colour change after clinical service and that such a colour change does not automatically necessitate replacement of the restoration. Chairside polishing should improve the stained appearance but it may not completely remove the stain to return the material to the original perceived shade.
DOI: 10.7860/JCDR/2022/57606.16627
Date of Submission: May 06, 2022
Date of Peer Review: May 20, 2022
Date of Acceptance: Jun 21, 2022
Date of Publishing: Jul 01, 2022
AUTHOR DECLARATION:
• Financial or Other Competing Interests: None
• Was Ethics Committee Approval obtained for this study? Yes
• Was informed consent obtained from the subjects involved in the study? NA
• For any images presented appropriate consent has been obtained from the subjects. NA
PLAGIARISM CHECKING METHODS:
• Plagiarism X-checker: May 11, 2022
• Manual Googling: May 19, 2022
• iThenticate Software: Jun 16, 2022 (10%)
ETYMOLOGY: Author Origin
- Emerging Sources Citation Index (Web of Science, thomsonreuters)
- Index Copernicus ICV 2017: 134.54
- Academic Search Complete Database
- Directory of Open Access Journals (DOAJ)
- Embase
- EBSCOhost
- Google Scholar
- HINARI Access to Research in Health Programme
- Indian Science Abstracts (ISA)
- Journal seek Database
- Popline (reproductive health literature)
- www.omnimedicalsearch.com